Basic characteristics of Q235 steel

Posted by Wangkiky Wangkiky over 6 months ago

In GB / T 700-2006, carbon structural steel Q235 is divided into four grades A, B, C and d according to metallurgical quality, and the chemical composition of each grade is Q235: Grade A, B, C and D (GB / T 700-2006)[url=http://www.anticorrosionsteel.com/steel-supply/516.html]GI Standard Outer Diameter 35mm Round Steel Tubes Pipes[/url] Q235 class A contains C ≤ 0.22%, Mn ≤ 1.4%, Si ≤ 0.35%, s ≤ 0.050 and P ≤ 0.045 Grade Q235B contains C ≤ 0.20%, Mn ≤ 1.4%, Si ≤ 0.35%, s ≤ 0.045 and P ≤ 0.045 (with the consent of the demander, the carbon content can not be greater than 0.22%) Q235C grade, C ≤ 0.17%, Mn ≤ 1.4%, Si ≤ 0.35%, s ≤ 0.040, P ≤ 0.040 Grade q235d, containing C ≤ 0.17%, Mn ≤ 1.4%, Si ≤ 0.35%, s ≤ 0.035 and P ≤ 0.035 There are many examples of manufacturing cold working dies by using low-carbon martensite rigid quenching process in China.[url=http://www.anticorrosionsteel.com/steel-supply/851.html]Astm Schedule 80 Carbon Steel Pipe Steel Seamless Pipe[/url] Using double glow plasma alloying technology, Mo CR co infiltration is carried out on the steel surface, followed by supersaturated carburizing, quenching and tempering. The thickness of Mo CR body layer is more than 100 microns, the surface Mo content can reach 20%, the Cr content can reach 10%, the carbon content of supersaturated Carburized surface can exceed 2.0%, the surface composition is close to molybdenum high-speed steel, and the surface hardness after quenching and tempering can reach 1300hv, More than general metallurgical high speed steel. The wear test shows that the friction coefficient increases with the increase of contact stress, and the average relative wear resistance is 2.2 times that of GCr15 carburized quenched steel.[url=http://www.anticorrosionsteel.com/steel-supply/6573.html]Best Sale 361 Stainless Steel 2x2 Tube Steel[/url]